Li8CaLa2Ta2O13:Sm3+荧光粉的可调发光和能量转移OA
Tunable Luminescence and Energy Transfer of Li8CaLa2Ta2O13:Sm3+Phosphors
通过高温固相法合成了一系列类石榴石结构的钽酸盐荧光粉 Li8CaLa2(1-x)Ta2O13:xSm3+(LCLTO:xSm3+).XRD 和 EDS 对晶体结构进行了确认,用荧光光谱仪考察所合成样品的发光性能.结果表明:在 234 nm激发下,基质与 Sm3+离子之间存在能量传递,通过调控 Sm3+离子掺杂浓度,实现从蓝色到粉红色的可调发光.在 406 nm波长激发下,最佳掺杂 LCLTO:0.06Sm3+荧光粉的最高发射峰位于 614 nm(4G5/2→6H7/2)处并发出橙红色光,有望用于近紫外光激发的白光 LED 中.
A novel tantalate phosphor with a garnet-like structure,Li8CaLa2(1-x)Ta2O13:xSm3+(LCLTO:xSm3+),was synthesized via a high-temperature solid-state reaction.The crystal structures were confirmed by XRD and EDS,and the luminescence properties of the synthesized samples were investigated using fluorescence spectroscopy.The results revealed that under 234 nm excitation,an energy transfer process existed from the host to Sm3+ion,which allows for tunable color emission from blue to pink by regulating the doping concentration of Sm3+ions.The optimal sample of LCLTO:0.06Sm3+exhibited orange-red light with the highest emission peak at 614 nm(4G5/2→6H7/2)when excited at 406 nm,which is anticipated to be utilized for near-UV excited white LED.
何嘉欣;曾帆;赵兵;茹晶晶;王冰燕
宁德师范学院 新能源与材料学院,福建 宁德 352100宁德师范学院 新能源与材料学院,福建 宁德 352100宁德师范学院 机电工程学院,福建 宁德 352100宁德师范学院 新能源与材料学院,福建 宁德 352100宁德师范学院 新能源与材料学院,福建 宁德 352100
数理科学
Li8CaLa2Ta2O13Sm3+掺杂荧光粉浓度猝灭能量转移
Li8CaLa2Ta2O13Sm3+dopingphosphorconcentration quenchingenergy transfer
《广州化学》 2026 (3)
43-47,5
福建省大学生创新创业项目(S202510398017)宁德师范学院校级科研项目(2024Y18,2023T03,2024ZX44)
评论