钌掺杂Ni(OH)2纳米片催化剂的制备及尿素电氧化性能OA
Synthesis and Urea Electrooxidation Performance of Ru-Doped Ni(OH)2 Nanosheet Catalysts
通过溶剂热合成法制备了钌掺杂氢氧化镍纳米片催化剂 Ru/Ni(OH)2,通过XRD、XPS、SEM 和 TEM 表征手段对 Ru/Ni(OH)2 复合催化剂的物相结构、形貌结构及元素价态进行了分析,并系统探究了金属钌掺杂对尿素电氧化催化性能强化规律.结果表明:通过构建的钌镍双活性位点共同促进了 UOR 性能,所制备的 Ru/Ni(OH)2-3 催化剂在 1 mol/L KOH/0.33 mol/L尿素电解液中仅需 1.39 V(vs RHE)即可达到 10 mA/cm2 的电流密度,其塔菲尔斜率为 49.80 mV/dec,且在 65000 s 持续电解后仍保持 86.12%的初始电流密度,表明其具有出色的催化性能和稳定性.
A ruthenium-doped nickel hydroxide nanosheet catalyst(Ru/Ni(OH)2)was synthesized via the solvothermal method.The phase structure,morphological characteristics,and elemental valence states of the Ru/Ni(OH)2 composite catalyst were analyzed using a series of physical characterization techniques(XRD,XPS,SEM and TEM).The enhancement mechanism of ruthenium doping on the electrocatalytic performance for the urea oxidation reaction(UOR)was systematically investigated.The experimental results demonstrate that the constructed ruthenium-nickel dual-active-site synergy promotes UOR performance.The prepared Ru/Ni(OH)2-3 catalyst requires only 1.39 V(vs.RHE)to achieve a current density of 10 mA/cm2 in a 1 mol/L KOH/0.33 mol/L urea electrolyte.It exhibits a Tafel slope of 49.80 mV/dec and maintains 86.12%of its initial current density after continuous electrolysis for 65,000 seconds.These results indicate outstanding catalytic performance and stability.
冯嘉璐;展思维;吴俊丽;赵欣阳;徐海涛
陕西理工大学 化学与环境科学学院,陕西省催化基础与应用重点实验室,陕西 汉中 723001陕西理工大学 化学与环境科学学院,陕西省催化基础与应用重点实验室,陕西 汉中 723001陕西理工大学 化学与环境科学学院,陕西省催化基础与应用重点实验室,陕西 汉中 723001陕西理工大学 化学与环境科学学院,陕西省催化基础与应用重点实验室,陕西 汉中 723001陕西理工大学 化学与环境科学学院,陕西省催化基础与应用重点实验室,陕西 汉中 723001
通用工业技术
尿素电氧化钌掺杂氢氧化镍双活性位点电催化
urea electrooxidationRu-dopingNi(OH)2dual active siteelectrocatalysis
《广州化学》 2026 (3)
27-33,7
陕西省大学生创新创业训练计划(S202410720085)陕西理工大学人才启动项目(SLGRCQD006)
评论