Ti/Al/Al/Fe层状多金属复合板的退火工艺研究OA
Study on Annealing Process of Ti/Al/Al/Fe Laminated Multimetallic Composite Plates
本文研究了不同退火工艺对温轧Ti/Al/Al/Fe层状多金属复合板(Laminated Multimetallic Composite Plates,LMCs)力学性能和界面微观组织的影响.结果表明,随着退火温度的升高,界面扩散层逐渐增厚,Ti/Al界面结合强度逐渐增加,Fe/Al界面拉剪强度则先降低再升高.在550℃/1 h退火时,Ti/Al/Al/Fe多金属复合板具有最佳的综合性能,抗拉强度为170 MPa,断后伸长率为52%.退火处理后,Ti/Al界面会形成TiAl3相,Fe/Al界面会形成FeAl3、Fe2Al5和Fe4Al13相,界面处由机械啮合为主导逐渐过渡到大面积的冶金结合.
Effects of different annealing processes on the mechanical properties and interfacial microstructure of warm-rolled Ti/Al/Al/Fe laminated multimetallic composite plates(LMCs)are investigated in this manuscript.The results indicate that with the increase of annealing temperature,the thickness of the interface diffusion layer gradually increases,the bonding strength of Ti/Al interface gradually increases,while the tensile shear strength of Fe/Al interface first decreases and then in-creases.When annealing at 550℃/1 h,Ti/Al/Al/Fe composite plates exhibit the best comprehensive properties,tensile strength(170 MPa)and elongation after break(52%).After annealing,TiAl3 phase is formed at the Ti/Al interface,while FeAl3,Fe2Al5,and Fe4Al13 phases are formed at the Fe/Al interface.The interface gradually transitions from mechanical mesh-ing to large-area metallurgical bonding.
臧浩浩;高翔;李骁;吕东旭;杨智显
新疆大学 材料科学与工程学院,新疆 乌鲁木齐 830017||新疆大学 新疆先进金属材料设计及应用重点实验室,新疆 乌鲁木齐 830017新疆大学 材料科学与工程学院,新疆 乌鲁木齐 830017||新疆大学 新疆先进金属材料设计及应用重点实验室,新疆 乌鲁木齐 830017新疆大学 材料科学与工程学院,新疆 乌鲁木齐 830017||新疆大学 新疆先进金属材料设计及应用重点实验室,新疆 乌鲁木齐 830017新疆大学 材料科学与工程学院,新疆 乌鲁木齐 830017||新疆大学 新疆先进金属材料设计及应用重点实验室,新疆 乌鲁木齐 830017新疆大学 材料科学与工程学院,新疆 乌鲁木齐 830017||新疆大学 新疆先进金属材料设计及应用重点实验室,新疆 乌鲁木齐 830017
通用工业技术
Ti/Al/Al/Fe复合板材退火工艺Ti/Al界面Fe/Al界面
Ti/Al/Al/Fe composite platesannealing processTi/Al interfaceFe/Al interface