Y2O3:Eu3+红色荧光粉的制备与发光性能研究OA
Preparation and Luminescent Properties of Y2O3:Eu3+Red Phosphors
采用水热-退火两步工艺制备系列Y2O3:xEu3+红色荧光粉,并研究Eu3+掺杂不同浓度对晶体结构和发光性能的影响.X射线衍射结果表明,样品均为立方相Y2O3,无杂相生成,Eu3+的引入导致晶格常数增大,表明其成功进入Y2O3晶格;荧光光谱表明,样品于611 nm处呈现最强红光发射,对应于Eu3+的5D0→7F2跃迁,随Eu3+掺杂浓度的增加,发光强度先增强后降低,当Eu3+掺杂摩尔分数为3％时,发射强度达到最大值,继续增加掺杂浓度则引发浓度猝灭现象;CIE色坐标表明,样品色坐标均在红光范围内,3％Eu3+掺杂样品色坐标最接近标准红光(0.64,0.33),表现出优异的色纯度.
A series of Y2O3:xEu3+red phosphors were prepared via a two-step hydrothermal-annealing method.The influence of Eu3+doping concentration on their crystal structure and luminescent performance was systematically studied.X-ray diffraction(XRD)results indicate that all samples possess a pure cubic Y2O3 phase without impuri-ty phases,and the increased lattice constant confirms the successful incorporation of Eu3+into the Y2O3 lattice.Photoluminescence(PL)spectra show that all samples emit the strongest red light at 611 nm,corresponding to the 5D0→7F2 transition of Eu3+.With the increase of Eu3+doping concentration,the emission intensity first increases and then decreases,reaching the maximum at a molar fraction of 3％,beyond which concentration quenching oc-curs.CIE chromaticity coordinates show that all samples are in the red light region,and the sample with 3％Eu3+has chromaticity coordinates closest to the standard red light(0.64,0.33),showing excellent color purity.
周雪;吴春雷;徐洪兵;贾思琦;赵立萍;左桂鸿;刘艳凤;孙明烨
牡丹江师范学院物理与电子工程学院,黑龙江 牡丹江 157011牡丹江师范学院物理与电子工程学院,黑龙江 牡丹江 157011牡丹江师范学院物理与电子工程学院,黑龙江 牡丹江 157011牡丹江师范学院物理与电子工程学院,黑龙江 牡丹江 157011牡丹江师范学院物理与电子工程学院,黑龙江 牡丹江 157011牡丹江师范学院物理与电子工程学院,黑龙江 牡丹江 157011牡丹江师范学院物理与电子工程学院,黑龙江 牡丹江 157011牡丹江师范学院物理与电子工程学院,黑龙江 牡丹江 157011
数理科学
Y2O3:Eu3+水热法红色荧光粉浓度猝灭
Y2O3:Eu3+hydrothermal methodred phosphorconcentration quenching