温度对新型航空复合材料IMA/M21X力学性能影响的试验研究OA
Experimental study on the effect of temperature on the mechanical properties of the new aeronautical composite material IMA/M21X
针对新型IMA/M21X复合材料的常用力学性能参数开展温度影响测试,对 0°和 90°铺层的试验件进行在常温、70℃、120℃、150℃和180℃工况下的拉伸试验,以及相应温度工况下剪切模量G12、G13 和G23 的测量.研究结果表明:横向弹性模量受温度影响大,从常温到 180℃下降了 34.78%;横向泊松比接近于 0 且随温度升高而升高;剪切模量均随温度升高而降低,与通常情况下认为G12=G13 不同,在常温下,该材料G12 比G13 大28.49%;IMA/M21X材料的拉伸模量和面内剪切模量相对更加优异,但层间剪切模量相对较弱.本研究取得了IMA/M21X材料的常温与温度力学参数,并探究了温度对其性能的影响,为该类材料的应用提供了基础.
Temperature influence tests were carried out for the commonly used mechanical properties parameters of the new IMA/M21X composites,and the tensile tests at room temperature,70℃,120℃,150℃,and 180℃were carried out for the 0° and 90° ply test specimens,as well as the measurements of the shear modulus G12,G13,and G23 at corresponding temperature conditions.The results show that the transverse modulus of elasticity is greatly affected by temperature,decreasing by 34.78%from room temperature to 180℃.Transverse Poisson's ratio approa-ches 0 and increases with increasing temperature.The shear modulus decreases with increasing temperature,unlike the usual assumption that G12=G13,at room temperature,the material G12 is 28.49%larger than G13.The tensile modulus and in-plane shear modulus of IMA/M21X material are relatively superior,but the inter layer shear modulus is relatively weak.The mechanical parameters of IMA/M21X at room temperature and temperature were obtained,and the effect of temperature on the properties of IMA/M21X was investigated.
赵彦淇;戴勇;刘畅;来晓靓;孙成;刘小林;邵纯
杭州电子科技大学 机械工程学院,杭州 310018上海航天设备制造总厂有限公司,上海 200240南京理工大学 机械工程学院,南京 210094浙江华瑞航空制造有限公司,杭州 310000浙江华瑞航空制造有限公司,杭州 310000浙江华瑞航空制造有限公司,杭州 310000杭州电子科技大学 机械工程学院,杭州 310018
通用工业技术
复合材料IMA/M21X温度试验力学性能
composite materialIMA/M21Xtemperatureexperimentmechanical properties
《复合材料科学与工程》 2026 (4)
1-8,8
浙江省自然科学基金(ZCLZ24A0201)浙江省高校基本科研业务费专项资金(GK249909299001-004)浙江省重点研发计划(2023C01009)浙江省"尖兵领雁+X"科技计划(2024SJCZX0034)浙江省教育厅科研项目(Y202455369)
评论