冻干法制备氮掺杂石墨烯负载Sb2S3钠离子电池负极材料OA
Synthesis of Nitrogen-Doped Graphene-Supported Antimony Sulfide Composite via Freeze-Drying Method for Sodium Ion Battery Anodes
钠储量丰富且成本低,因此钠离子电池具有广阔的发展前景.其中,转化型负极材料 Sb2S3因具备较高的理论比容量而被广泛关注.本研究采用冷冻干燥法制备的氮掺杂石墨烯负载硫化锑复合材料(Sb2S3@NG),具有高连通性的三维导电网络,为体积膨胀提供更多缓冲空间.结 果 表 明:Sb2S3@NG 在 0.1,A/g 电流密度下,比容量高达1,079.7 mA·h/g,首圈库仑效率为 86.3%;在 0.5,A/g 电流密度下循环 150 圈后比容量仍为 578.8,mA·h/g,容量保持率为82.5%.
Sodium-ion batteries(SIBs)hold great potential for energy storage applications due to the abundant sodium re-serves and low cost.Conversion-type Sb2S3 has attracted significant research attention owing to its high theoretical specific capacity.In this study,a nitrogen-doped graphene-supported antimony sulfide composite(Sb2S3@NG)was synthesized via a freeze-drying method.The introduction of nitrogen-doped graphene facilitates the construction of a highly interconnected three-dimensional conductive network,providing additional buffer space to accommodate volume expansion.The study re-sults demonstrated that Sb2S3@NG exhibited a high specific capacity of 1 079.7 mA·h/g at a current density of 0.1 A/g,with an initial Coulombic efficiency of 86.3%.Furthermore,after 150 cycles at 0.5 A/g,the composite retained a reversible cap-acity of 578.8 mA·h/g,corresponding to a capacity retention rate of 82.5%.
陈雪;李亚斌;赵子健;贾原媛;王彦飞
天津科技大学化工与材料学院,天津 300457||天津市卤水化工与资源生态化利用重点实验室,天津 300454||天津市海洋化工技术工程中心,天津 300454天津大学化工学院,天津 300350天津科技大学化工与材料学院,天津 300457||天津市卤水化工与资源生态化利用重点实验室,天津 300454||天津市海洋化工技术工程中心,天津 300454天津科技大学化工与材料学院,天津 300457||天津市卤水化工与资源生态化利用重点实验室,天津 300454||天津市海洋化工技术工程中心,天津 300454天津科技大学化工与材料学院,天津 300457||天津市卤水化工与资源生态化利用重点实验室,天津 300454||天津市海洋化工技术工程中心,天津 300454
通用工业技术
钠离子电池负极材料硫化锑掺氮石墨烯
sodium-ion batteryanode materialSb2S3nitrogen-doped graphene
《天津科技大学学报》 2026 (2)
54-59,66,7