Analysis of Radar Cross Sections for aluminum targets in terahertz band at different temperatures
太赫兹频段金属材质反射率随温度的变化规律对于太赫兹目标主被动融合探测的研究具有重要意义.本文聚焦金属铝材质,通过与文献以及实测结果对比,验证扩展Hagen-Rubens理论公式适用于研究金属在太赫兹频段的反射性能.选取0.1 THz、0.2 THz、0.5 THz、1.0 THz、10 THz五个典型太赫兹频点计算了 273～933 K范围内金属铝材质的反射率,发现随着温度的升高,在太赫兹频段金属铝材质的反射率逐渐降低且反射率变化不超过0.02.分析了不同温度下的典型金属铝球、正方形铝薄板和圆柱体的太赫兹雷达散射截面积(RCS)随温度的变化规律,结果表明,目标RCS在273～933K范围内缓慢变小,且变化量不超过0.05dB.
The temperature-dependent variation of metal material reflectivity in the terahertz band is of great significance for research on active-passive fusion detection of terahertz targets.This paper focuses on metallic aluminum,and by comparing with literature and measured results,verifies that the extended Hagen-Rubens theoretical formula is applicable for studying the reflection performance of metals in the terahertz band.Five typical terahertz frequency points of 0.1,0.2,0.5,1.0 and 10 THz are selected to calculate the reflectivity of metallic aluminum within the temperature range of 273～933 K.It is found that as temperature increases,the reflectivity of metallic aluminum in the terahertz band gradually decreases,with the reflectivity variation not exceeding 0.02.The temperature-dependent variation of terahertz Radar Cross Section(RCS)is analyzed for typical metallic aluminum spheres,square aluminum thin plates,and cylinders at different temperatures.The results indicate that the target RCS slowly decreases within the 273～933 K range,with the variation not exceeding 0.05 dB.
陈刚;李浩;何征;张娜;刘灵鸽;卢海梁;牛文博;党红杏;李一楠;吕容川
中国空间技术研究院西安分院,陕西西安 710100中国空间技术研究院西安分院,陕西西安 710100中国空间技术研究院西安分院,陕西西安 710100北京无线电计量测试研究所,北京 100854中国空间技术研究院西安分院,陕西西安 710100湖北珞珈实验室,湖北武汉 430079中国空间技术研究院西安分院,陕西西安 710100中国空间技术研究院西安分院,陕西西安 710100中国空间技术研究院西安分院,陕西西安 710100中国空间技术研究院西安分院,陕西西安 710100
信息技术与安全科学
太赫兹散射温度变化反射率雷达散射截面积(RCS)
terahertz wavescatteringtemperature changereflectivityRadar Cross Sections(RCS)
《太赫兹科学与电子信息学报》 2026 (2)
236-241,6
评论