Al2O3包覆对LiNi0.5Co0.2Mn0.3O2电化学性能的影响OA
Effect of Al2O3 coating on electrochemical performance of LiNi0.5Co0.2Mn0.3O2
表面包覆是延缓锂离子电池正极材料老化的重要手段.调控煅烧温度制备α、θ、δ和γ晶型氧化铝(Al2O3)包覆层材料,研究包覆层对LiNi0.5Co0.2Mn0.3O2(NCM523)正极材料性能的影响.Al2O3涂层能提升正极材料的电化学性能,包覆层可抑制活性材料与电解质之间的界面副反应,减少过渡金属离子的溶解,并提高材料的结构稳定性.采用Al2O3包覆正极所组装的电池,在3.0～4.3 V充放电,5.0 C高倍率下表现出115.3 mAh/g的放电比容量;并且在1.0 C条件下循环300次后仍具有124.1 mAh/g的放电比容量.
Surface coating is an important means to delay the aging of cathode materials in Li-ion batteries.The aluminum oxide(Al2O3)coating materials with α,θ,δ and γ crystalline phases are prepared by adjusting the calcination temperature,the effect of the coating layer on the performance of LiNi0.5Co0.2Mn0.3O2(NCM523)cathode material is studied.The Al2O3 coatings enhance the electrochemical performance of the cathode material.The coating layers suppress interfacial side reactions between the active material and the electrolyte,reduce the dissolution of transition metal ions,and improve the structural stability of the material.When charged and discharged in 3.0-4.3 V,batteries assembled with the Al2O3-coated cathode exhibit a discharge specific capacity of 115.3 mAh/g at a high rate of 5.0 C and maintain a discharge specific capacity of 124.1 mAh/g after 300 cycles at 1.0 C.
李芳润;陈海波;李杭;胡敬;张健力;陈强;侯广亚;唐谊平
浙江工业大学材料科学与工程学院,浙江 杭州 310014浙江工业大学材料科学与工程学院,浙江 杭州 310014浙江工业大学材料科学与工程学院,浙江 杭州 310014浙江工业大学材料科学与工程学院,浙江 杭州 310014浙江工业大学材料科学与工程学院,浙江 杭州 310014浙江工业大学材料科学与工程学院,浙江 杭州 310014浙江工业大学材料科学与工程学院,浙江 杭州 310014浙江工业大学材料科学与工程学院,浙江 杭州 310014
信息技术与安全科学
锂离子电池正极材料LiNi0.5Co0.2Mn0.3O2(NCM523)Al2O3包覆
Li-ion batterycathode materialLiNi0.5Co0.2Mn0.3O2(NCM523)Al2O3 coating
《电池》 2026 (1)
30-36,7
国家自然科学基金面上项目(52271039),国家自然科学基金青年科学基金项目(52202315,52202313),浙江省尖兵领雁研发计划(2025C01182),浙江省自然科学基金(LZ22E010002,LQ22E020005)
评论