不同强度低熟料固废基混凝土制备及其性能OA
Preparation and Properties of Low Clinker Solid Waste Based Concrete with Different Strength
本实验采用粒化高炉矿渣粉、脱硫石膏等制备了低熟料固废基水泥,研究了不同强度等级低熟料固废基水泥制备的混凝土物理力学性能,分析了力学性能与吸水率、干缩应变之间的关系.结果表明:砂率与胶凝材料用量升高可以显著改善低熟料固废基混凝土拌合物的工作性能;不同强度等级低熟料固废基混凝土 7 d至28 d抗压强度的增长幅度均超过65％以上,28 d至60 d的抗压强度增长幅度均超过20％;低熟料固废基混凝土的吸水率与干缩应变随着强度等级的提升而显著降低;不同强度等级低熟料固废基混凝土试样的吸水率与干缩应变均与抗压强度呈二次函数关系.
Low clinker solid waste based concrete was prepared using granulated blast furnace slag micronized powder.The physical and mechanical properties of different strength low clinker solid waste based concrete were studied.The relationship between mechanical properties and water absorption,dry shrinkage strain was analyzed.Results showed that the compressive strength of different strength concrete increased by 65％from 7 d to 28 d and 20％from 28 d to 60 d.The water absorption and dry shrinkage strain of concrete decreased significantly with the increase of strength grade.The relationship between water absorption or dry shrinkage strain and compressive strength of different strength concrete is quadratic function.
焦晓东;李辉;熊剑平;刘文欢
西安建筑科技大学材料科学与工程学院,陕西西安 710055||广西道路结构与材料重点实验室,广西南宁 530007||广西交科集团有限公司,广西南宁 530007西安建筑科技大学材料科学与工程学院,陕西西安 710055||教育部生态水泥工程研究中心,陕西西安 710055广西道路结构与材料重点实验室,广西南宁 530007||广西交科集团有限公司,广西南宁 530007西安建筑科技大学材料科学与工程学院,陕西西安 710055||教育部生态水泥工程研究中心,陕西西安 710055
建筑与水利
低熟料固废基混凝土收缩性能孔结构强度
Low clinker solid waste based concreteShrinkage performancePore structureStrength