碳纳米管纤维的强度增强及其在抛光领域的应用OA
Increasing the strength of carbon nanotube fibers and their use as a polishing medium
本研究提出了一种双功能策略,通过引入聚乙烯亚胺,在提升碳纳米管(CNT)纤维力学强度的同时实现氧化铈(CeO2)磨粒在其表面的均匀粘附.结果显示,5%的PEI可使CNT纤维的拉伸强度相较于原始纤维提高约175%.此外,通过电泳沉积法,CeO2 颗粒均匀地沉积在增强后的CNT纤维上.将 CeO2/CNT复合纤维编织在无纺布基底上,进而制作出一种柔性抛光工具.在对磷酸二氢钾晶体进行抛光处理时,该工具能在10 min内将晶体表面粗糙度从200降至7.6 nm.这种创新方法为新型精密加工工具的开发带来了较大的潜力.
We report a method for increasing the mechanical strength of carbon nanotube(CNT)fibers while enabling the uni-form adhesion of cerium oxide(CeO2)abrasive particles to them using polyethyleneimine(PEI).Results show that 5%of PEI in-creases the tensile strength of CNT fibers by approximately 175%.CeO2 particles were uniformly deposited on the rein-forced CNT fibers by electrophoretic deposition.A flexible polishing tool was fabricated by weaving the CeO2-CNT fibers into a non-woven fabric substrate.When used to polish potassium dihydrogen phosphate crystals,the tool reduced the surface roughness from 200 to 7.6 nm within 10 min.This approach has potential use for the development of new precision processing tools.
薛志萍;陆静;黄辉
华侨大学 制造工程研究院,福建 厦门 361021||华侨大学 "脆性材料产品智能制造技术"国家地方联合工程研究中心,福建 厦门 361021||华侨大学 高性能工具全国重点实验室,福建 厦门 361021||华侨大学 生物质低碳转化福建省高校重点实验室,福建 厦门 361021华侨大学 制造工程研究院,福建 厦门 361021||华侨大学 "脆性材料产品智能制造技术"国家地方联合工程研究中心,福建 厦门 361021||华侨大学 高性能工具全国重点实验室,福建 厦门 361021||华侨大学 生物质低碳转化福建省高校重点实验室,福建 厦门 361021华侨大学 制造工程研究院,福建 厦门 361021||华侨大学 "脆性材料产品智能制造技术"国家地方联合工程研究中心,福建 厦门 361021||华侨大学 高性能工具全国重点实验室,福建 厦门 361021
化学化工
碳纳米管纤维拉伸强度电泳沉积抛光工具表面粗糙度
CNT fiberTensile strengthElectrophoretic depositionPolishing toolSurface roughness
《新型炭材料（中英文）》 2026 (1)
209-221,13
The authors appreciate financial support from the Natural Science Foundation of Xiamen(3502Z202472015),the Major Science and Techno-logy Project of Xiamen(3502Z20231047),and the Open Research Fund of Academy of Advanced Car-bon Conversion Technology,Huaqiao University.厦门市自然科学基金项目(3502z202472015)厦门市重大科技专项(3502z20231047)和华侨大学先进碳转化技术研究院开放研究基金.