Yb∶YAP单晶光纤的生长及光谱性能研究OA
Growth and Spectral Properties of Yb∶YAP Crystal Fibers
采用微下拉法成功生长了系列不同掺杂浓度Yb∶YAlO(3 Yb∶YAP)单晶光纤.X射线衍射分析证实所得单晶光纤均为正交晶系.在室温下系统测试了样品的吸收光谱、荧光光谱和荧光衰减曲线.2.00%(原子数分数)Yb∶YAP单晶光纤在978 nm处的吸收截面为1.14×10-20 cm2,在1 000 nm的最大发射截面达1.39×10-20 cm2,显示出与商用激光二极管泵浦源良好的光谱匹配性.0.25%、0.50%、1.00%、2.00%和5.00%Yb∶YAP单晶光纤中 2F5/2能级荧光寿命分别为587、604、682、705和698 µs.结果表明Yb∶YAP单晶光纤是一种有潜力的超快激光增益介质.
Yb3+-doped YAlO3(Yb∶YAP)crystal fibers with different doping concentrations were successfully grown using the micro-pulling-down method.X-ray diffraction(XRD)characterization verified their orthorhombic crystal structure.Absorption spectra,fluorescence spectra and fluorescence decay curves were systematically measured at room temperature.For the 2.00%(atomic fraction)doped sample,the absorption cross-section at 978 nm reaches 1.14×10-20 cm2,while the maximum emission cross-section at 1 000 nm is 1.39×10-20 cm2,showing good spectral compatibility with commercially available laser diodes.The measured 2F5/2 level lifetime for 0.25%,0.50%,1.00%,2.00%and 5.00%Yb∶YAP crystal fibers are 587,604,682,705 and 698 µs,respectively.These results collectively indicate that Yb∶YAP crystal fibers are promising gain media for ultrafast laser applications.
汪晨;徐军;张家玮;张华利;周声浪;刘龙鑫;姜正元;张俊;刘坚;徐晓东
江苏协鑫硅材料科技发展有限公司,徐州 221000同济大学物理科学与工程学院,上海 200092江苏师范大学物理与电子工程学院,徐州 221116江苏协鑫硅材料科技发展有限公司,徐州 221000江苏协鑫硅材料科技发展有限公司,徐州 221000江苏师范大学物理与电子工程学院,徐州 221116江苏师范大学物理与电子工程学院,徐州 221116江苏师范大学物理与电子工程学院,徐州 221116江苏师范大学物理与电子工程学院,徐州 221116江苏师范大学物理与电子工程学院,徐州 221116
数理科学
微下拉法单晶光纤Yb∶YAP晶体生长光谱性能
micro-pulling-down methodcrystal fiberYb∶YAPcrystal growthspectral property