基于陶瓷基板的焊接润湿性及失效机理研究OA

The solder will scatter and wet on the surface of the solder pad during the welding process.The wetting effect is closely related to the surface tension of the solder,the surface state of the solder pad,and the welding conditions.If solder wetting is poor,it will directly affect the welding area and the welding strength,which will ultimately reduce the welding reliability of the product.Poor wetting occurred during welding of a certain ceramic substrate,and the appearance and composition of the shearing fracture surface are analyzed by scanning electron microscopy and energy-dispersive spectroscopy,and the welding interface is analyzed by slicing.It is found that the nickel layer of the solder pad is too thin,finally leading to the poor wetting.Some countermeasures are presented.