用于黑磷锂电池负极的聚合物黏结剂制备及性能研究OA
Preparation and performance of polymeric binders for black phosphorus-based negative electrode
以锂离子电池电极常用的聚偏氟乙烯及羧甲基纤维素、聚丙烯酸、海藻酸钠等为黏结剂,研究了黏结剂组成结构对新型黑磷基负极材料的影响规律.通过溶胀性、剥离性,浸润性和扫描电子显微镜(SEM)等方法对电极材料进行测试表征,并测试了电池的电化学循环性稳定及倍率性能.结果表明,聚丙烯酸黏结剂电池的比容量、循环稳定性、倍率性等综合性能最好,在0.5 A/g的电流密度下,首次可逆比容量高达1 960.4 mAh/g,循环50圈后的容量保持率高达89.3%.
In this study,the influence of binder composition and structure on the performance of black phosphorus-based anodes for lithium-ion batteries was investigated by using four binders,polyvinylidene fluoride,carboxymethyl cellulose,polyacrylic acid,and sodium alginate.The electrodes were characterized through swelling,peeling,wetting,and scan-ning electron microscopy tests,while their electrochemical performance was assessed in terms of cycle stability and rate capability.Results demonstrated that the electrode utilizing a polyacrylic acid binder delivered the optimal comprehensive performance,exhibiting superior specific capacity,cycling stability,and rate performance.This electrode achieved a first reversible specific capacity of 1 960.4 mAh/g at a current density of 0.5 A/g and maintained a high capacity retention of 89.3%after 50 cycles.
王睿褀;肖芳莉;郑亚楠;祖雷;刘洋;汪晓东;连慧琴
北京石油化工学院新材料与化工学院,特种弹性体复合材料北京市重点实验室,北京 102617北京石油化工学院新材料与化工学院,特种弹性体复合材料北京市重点实验室,北京 102617北京石油化工学院新材料与化工学院,特种弹性体复合材料北京市重点实验室,北京 102617北京石油化工学院新材料与化工学院,特种弹性体复合材料北京市重点实验室,北京 102617北京石油化工学院新材料与化工学院,特种弹性体复合材料北京市重点实验室,北京 102617北京化工大学有机无机复合材料全国重点实验室,北京 100029北京石油化工学院新材料与化工学院,特种弹性体复合材料北京市重点实验室,北京 102617
化学化工
锂离子电池黏结剂聚甲基丙烯酸比容量倍率性能
lithium-ion batteriesbinderpoly(methyl methacrylate)specific capacityrate capability
《中国塑料》 2026 (1)
50-56,7
国家自然科学基金(51573021、51203012)北京市自然科学基金(2162015)大学生研究训练项目(2023J00057、2023J00153)
评论